详细信息
Typical Tensile Properties
As welded Elongation Tensile Strength Yield Strength 36 % 570 MPa 400 MPa Tested at 350°C. As welded Elongation Tensile Strength Yield Strength 25 % 490 MPa 370 MPa 夏比V型缺口冲击性能
As welded Impact Value Testing Temperature 110 J 20 °C 70 J -60 °C 45 J -196 °C 焊缝金属分析
Mn Mn Mo Cu C Si Ferrite FN Ni Cr 1.8 % - - - - - - - Mo Mn Mo Cu C Si Ferrite FN Ni Cr - 0.15 % - - - - - - Cu Mn Mo Cu C Si Ferrite FN Ni Cr - - 0.10 % - - - - - C Mn Mo Cu C Si Ferrite FN Ni Cr - - - 0.01 % - - - - Si Mn Mo Cu C Si Ferrite FN Ni Cr - - - - 0.9 % - - - Ferrite FN Mn Mo Cu C Si Ferrite FN Ni Cr - - - - - 9 % - - Ni Mn Mo Cu C Si Ferrite FN Ni Cr - - - - - - 10.5 % - Cr Mn Mo Cu C Si Ferrite FN Ni Cr - - - - - - - 19.9 % 熔敷数据
直径 安培 熔敷率 电压 V 送丝速度 0.6 mm - - - - 0.8 mm 55-160 A 1.0-4.1 kg/h 15-24 V 4.0-17.0 m/min 0.9 mm 65-220 A 1.1-5.4 kg/h 15-28 V 3.5-18.0 m/min 1.0 mm 80-240 A 1.5-6.0 kg/h 15-28 V 4.0-16.0 m/min 1.14 mm - - - - 1.2 mm 100-300 A 1.6-7.5 kg/h 15-29 V 3.0-14.0 m/min 1.6 mm 230-375 A 5.2-8.6 kg/h 23-29 V 5.5-9.0 m/min