适用于焊接类似和匹配钢材且含有18% Cr并采用0.5% Ti稳定化的铁素体不锈钢实芯焊丝。该合金通常用于非合金钢和低合金钢的熔敷。 OK Autrod 430Ti还在汽车行业的歧管、催化转换器和排气管焊接上得到广泛应用。
Typical Tensile Properties
| Stress relieved |
| Elongation |
Stress Relieved Temperature |
Stress Relieved Testing Time |
Tensile Strength |
Yield Strength |
| 24 % |
780 °C |
0.5 hr |
600 MPa |
390 MPa |
| 28 % |
780 °C |
0.5 hr |
580 MPa |
380 MPa |
焊缝金属分析
| Mn |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| 0.5 % |
- |
- |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
0.05 % |
- |
- |
- |
- |
- |
- |
| Cu |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
0.10 % |
- |
- |
- |
- |
- |
| C |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
- |
0.07 % |
- |
- |
- |
- |
| Ti |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.400 % |
- |
- |
- |
| Si |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
0.9 % |
- |
- |
| Ni |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
- |
0.3 % |
- |
| Cr |
| Mn |
Mo |
Cu |
C |
Ti |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
- |
- |
17.6 % |
熔敷数据
| 直径 |
安培 |
熔敷率 |
电压 V |
送丝速度 |
| 0.9 mm |
- |
- |
- |
- |
| 1.0 mm |
80-190 A |
1,1-3,1 kg/h |
16-24 V |
2,9-8,4 m/min |
| 1.2 mm |
180-280 A |
2,6-4,5 kg/h |
20-28 V |
4,9-8,5 m/min |
| 1.6 mm |
230-350 A |
3-5,2 kg/h |
24-28 V |
3,2-5,5 m/min |