适用于焊接25% Cr, 7% Ni, 4% Mo,低碳奥氏体铁素体不锈钢的实芯抗腐蚀“超级双相”合金焊丝。 OK Autrod 2509具有较高的抗晶间腐蚀性、抗点蚀性和抗应力腐蚀性。该合金广泛用于抗腐蚀性具有极其重要性的应用。其适用于纸浆和造纸行业、海洋工程和天然气行业。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
| 30 % |
832 MPa |
659 MPa |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
| 159 J |
20 °C |
| 129 J |
-40 °C |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| 0.4 % |
- |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| - |
3.9 % |
- |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| - |
- |
0.01 % |
- |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
0.4 % |
- |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
- |
9.4 % |
- |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
- |
- |
- |
25.2 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 80-190 A |
1,1-3,1 kg/h |
16-24 V |
1.0 mm |
2,9-8,4 m/min |
| 180-280 A |
2,6-4,5 kg/h |
20-28 V |
1.2 mm |
4,9-8,5 m/min |