适用于焊接21% Cr-1% Ni或23% Cr-4% Ni型奥氏体-铁素体不锈钢的实芯抗腐蚀双相焊丝。OK Autrod 2307经过Ni的超合金化处理，可确保焊缝金属中适当的铁素体平衡。 低镍双相型焊丝可用于土木工程、储罐、容器等的焊接。此类钢材一般具有中等抗腐蚀性和优良的强度性能。 焊接方式与普通奥氏体钢相同，但应避免电流过高，并且层间温度*大不超过150°C。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
| 32 % |
730 MPa |
560 MPa |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
| 160 J |
20 °C |
| 60 J |
-60 °C |
焊缝金属分析
| Mn |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| 1.4 % |
- |
- |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
3.20 % |
- |
- |
- |
- |
- |
- |
| Cu |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
- |
0.2 % |
- |
- |
- |
- |
- |
| C |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
0.01 % |
- |
- |
- |
- |
| Si |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
- |
0.5 % |
- |
- |
- |
| Ni |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
- |
- |
7.1 % |
- |
- |
| Cr |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
N |
Cr |
| - |
- |
- |
- |
- |
- |
- |
23.2 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 80-190 A |
1,1-3,1 kg/h |
16-24 V |
1.0 mm |
2,9-8,4 m/min |
| 180-280 A |
2,6-4,5 kg/h |
20-28 V |
1.2 mm |
4,9-8,5 m/min |