适用于焊接18% Cr-8% Ni-7% Mn牌号奥氏体不锈钢的实芯抗腐蚀铬镍锰合金焊丝。 OK Autrod 16.95具有与相应母材类似的普通抗腐蚀性。较高的硅含量改善了诸如熔湿性之类的焊接性能。该产品为ER307的改良型号，主要利用较高的锰含量降低焊缝的热裂纹敏感性。在用于焊接异种材料时，抗腐蚀性的重要性位居其次。该合金可用于诸如奥氏体钢、锰钢、工作硬化钢以及装甲板和耐热钢的各种应用。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
| 41 % |
640 MPa |
450 MPa |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
| 130 J |
20 °C |
焊缝金属分析
| Mn |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| 7.0 % |
- |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
0.20 % |
- |
- |
- |
- |
- |
| Cu |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
- |
0.10 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.08 % |
- |
- |
- |
| Si |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.9 % |
- |
- |
| Ni |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
8.1 % |
- |
| Cr |
| Mn |
Mo |
Cu |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
- |
18.7 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 55-160 A |
1.0-4.1 kg/h |
15-24 V |
0.8 mm |
4.0-17.0 m/min |
| 65-220 A |
1.1-5.4 kg/h |
15-28 V |
0.9 mm |
3.5-18.0 m/min |
| 80-240 A |
1.5-6.0 kg/h |
15-28 V |
1.0 mm |
4.0-16.0 m/min |
| 100-300 A |
1.6-7.5 kg/h |
15-29 V |
1.2 mm |
3.0-14.0 m/min |
| 230-375 A |
5.2-8.6 kg/h |
23-31 V |
1.6 mm |
5.5-9.0 m/min |