适用于诸如容器、管道及海洋工程应用中*小屈服强度低于470 Mpa低合金及低温钢种GMAW焊接的镀铜镍合金(2,4% Ni)实芯焊丝。该焊丝在-60°C条件下具有良好的冲击韧性。
Typical Tensile Properties
| Stress relieved |
| Elongation |
Stress Relieved Temperature |
Stress Relieved Testing Time |
Tensile Strength |
Yield Strength |
保护气体 |
| 29 % |
620 °C |
1 hr |
630 MPa |
540 MPa |
AWS Ar/1-5O2 (M13) |
| As welded |
| Elongation |
Stress Relieved Temperature |
Stress Relieved Testing Time |
Tensile Strength |
Yield Strength |
保护气体 |
| 28 % |
- |
- |
630 MPa |
540 MPa |
EN Ar/20CO2(M21) |
夏比V型缺口冲击性能
| Stress relieved |
| Impact Value |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
Testing Temperature |
保护气体 |
| 162 J |
620 °C |
1 hr |
0 °C |
AWS Ar/1-5O2 (M13) |
| 168 J |
620 °C |
1 hr |
-29 °C |
AWS Ar/1-5O2 (M13) |
| 131 J |
620 °C |
1 hr |
-62 °C |
AWS Ar/1-5O2 (M13) |
| As welded |
| Impact Value |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
Testing Temperature |
保护气体 |
| 130 J |
- |
- |
0 °C |
EN Ar/20CO2(M21) |
| 100 J |
- |
- |
-40 °C |
EN Ar/20CO2(M21) |
| - |
- |
- |
-50 °C |
EN Ar/20CO2(M21) |
| 60 J |
- |
- |
-60 °C |
EN Ar/20CO2(M21) |
焊缝金属分析
| Mn |
| Mn |
C |
Si |
Ni |
Cr |
| 1.04 % |
- |
- |
- |
- |
| C |
| Mn |
C |
Si |
Ni |
Cr |
| - |
0.08 % |
- |
- |
- |
| Si |
| Mn |
C |
Si |
Ni |
Cr |
| - |
- |
0.53 % |
- |
- |
| Ni |
| Mn |
C |
Si |
Ni |
Cr |
| - |
- |
- |
2.36 % |
- |
| Cr |
| Mn |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.03 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 40-170 A |
0,4-2,6 kg/h |
16-22 V |
0.8 mm |
2-10,8 m/min |
| 80-280 A |
1-5,4 kg/h |
18-28 V |
1.0 mm |
2,7-14,7 m/min |
| 120-350 A |
1,5-6,6 kg/h |
20-33 V |
1.2 mm |
2,7-12,4 m/min |