OK AristoRod™ 13.09是一种适适用于抗蠕变钢GMAW焊接的0.5Mo合金化实芯焊丝，该抗蠕变钢与500°C工作温度下压力容器与锅炉管道使用材料的成分相同。OK AristoRod™ 13.09经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。
Typical Tensile Properties
| As welded+ |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
| 20 % |
570 MPa |
425 MPa |
80Ar/20CO2 |
- |
- |
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
| 26 % |
630 MPa |
515 MPa |
80Ar/20CO2 |
- |
- |
| Stress relieved |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
| 23 % |
490 MPa |
370 MPa |
80Ar/20CO2 |
620 °C |
15 hr |
| 26 % |
545 MPa |
430 MPa |
80Ar/20CO2 |
620 °C |
15 hr |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
| 117 J |
20 °C |
80Ar/20CO2 |
- |
- |
| 75 J |
-20 °C |
80Ar/20CO2 |
- |
- |
| 57 J |
-40 °C |
80Ar/20CO2 |
- |
- |
| Stress relieved |
| Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
| 150 J |
20 °C |
80Ar/20CO2 |
620 °C |
15 hr |
| 130 J |
0 °C |
80Ar/20CO2 |
620 °C |
15 hr |
| 95 J |
-20 °C |
80Ar/20CO2 |
620 °C |
15 hr |
| 90 J |
-40 °C |
80Ar/20CO2 |
620 °C |
15 hr |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| 1.09 % |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
0.45 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
0.094 % |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.61 % |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.04 % |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
0.07 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 40-170 A |
0,4-2,6 kg/h |
16-22 V |
0.8 mm |
2-10,8 m/min |
| 80-280 A |
1-5,4 kg/h |
18-28 V |
1.0 mm |
2,7-14,7 m/min |
| 120-350 A |
1,5-6,6 kg/h |
20-33 V |
1.2 mm |
2,7-12,4 m/min |
| 225-480 A |
3,3-11.6 kg/h |
26-38 V |
1.6 mm |
3,10-12 m/min |