OK AristoRod™ 13.08是一种适用于抗蠕变钢GMAW焊接的0.4Mo合金化(ER80S-D2)实芯焊丝，该抗蠕变钢与500°C工作温度下使用材料的成分相同。AristoRod™ 13.08经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 25 % |
645 MPa |
540 MPa |
AWS CO2 (C1) |
| 24 % |
685 MPa |
590 MPa |
EN 80Ar/20CO2 (M21) |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
| 90 J |
20 °C |
AWS CO2 (C1) |
| 36 J |
-20 °C |
AWS CO2 (C1) |
| - |
-29 °C |
AWS CO2 (C1) |
| 38 J |
-40 °C |
AWS CO2 (C1) |
| 140 J |
20 °C |
EN 80Ar/20CO2 (M21) |
| 100 J |
-20 °C |
EN 80Ar/20CO2 (M21) |
| 80 J |
-40 °C |
EN 80Ar/20CO2 (M21) |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| 1.78 % |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
0.47 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
0.098 % |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.6 % |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.05 % |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
0.04 % |
熔敷数据
| 安培 |
熔敷率 |
电压 V |
直径 |
送丝速度 |
| 40-170 A |
0,4-2,6 kg/h |
16-22 V |
0.8 mm |
2-10,8 m/min |
| 70-280 A |
1-5,4 kg/h |
18-28 V |
0.9 mm |
2,7-14,7 m/min |
| 90-300 A |
1-5,4 kg/h |
18-28 V |
1.0 mm |
2,7-14,7 m/min |
| 120-350 A |
1,5-6,6 kg/h |
20-33 V |
1.2 mm |
2,7-12,4 m/min |
| 225-480 A |
3,3-11.6 kg/h |
26-38 V |
1.6 mm |
3,10-12 m/min |