OK Tigrod 13.37是一种适用于高温钢和炼油厂热氢环境用钢GTAW焊接的9Cr-1Mo合金化镀铜焊丝。该焊焊丝为普通ER505型。
Typical Tensile Properties
| Stress relieved |
| Elongation |
Stress Relieved Temperature |
Stress Relieved Testing Time |
Tensile Strength |
Yield Strength |
保护气体 |
| 22 % |
735 °C |
4 hr |
680 MPa |
560 MPa |
Ar (I1) EN |
| 26 % |
760 °C |
2 hr |
660 MPa |
540 MPa |
Ar (I1) EN |
| 22 % |
760 °C |
2 hr |
390 MPa |
350 MPa |
Enhanced testing temperature. |
| 18 % |
760 °C |
2 hr |
480 MPa |
410 MPa |
Enhanced testing temperature. |
| 17 % |
760 °C |
2 hr |
500 MPa |
430 MPa |
Enhanced testing temperature. |
夏比V型缺口冲击性能
| Stress relieved |
| Impact Value |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
Testing Temperature |
保护气体 |
| 150 J |
735 °C |
4 hr |
-20 °C |
Ar (I1) EN |
| 130 J |
735 °C |
4 hr |
-40 °C |
Ar (I1) EN |
| 50 J |
735 °C |
4 hr |
-60 °C |
Ar (I1) EN |
| 140 J |
760 °C |
2 hr |
-20 °C |
Ar (I1) EN |
| 120 J |
760 °C |
2 hr |
-40 °C |
Ar (I1) EN |
| 90 J |
760 °C |
2 hr |
-60 °C |
Ar (I1) EN |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| 0.52 % |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
1.00 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
0.06 % |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.45 % |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.23 % |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
8.66 % |
熔敷数据
| 安培 |
直径 |
| 40-180 A |
1.6 mm |
| 60-200 A |
2.0 mm |
| 100-220 A |
2.4 mm |
| 130-250 A |
3.2 mm |