OK Tigrod 13.32是一种适用于类似成分抗蠕变钢GTAW焊接的5Cr-0.5Mo合金化(ER80S-B6)镀铜焊丝。该焊丝还适合用于焊接*小屈服强度达730 MPa的高强度钢。 AWS已对该产品的归类进行修改。此前归类编号为A5.9 ER502。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
| 22 % |
900 MPa |
730 MPa |
Ar (I1) AWS |
- |
- |
| Stress relieved |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
Stress Relieved Temperature |
Stress Relieved Testing Time |
| 22 % |
680 MPa |
580 MPa |
Ar (I1) AWS |
745 °C |
1 hr |
| 19 % |
477 MPa |
430 MPa |
Ar (I1) EN |
730-760 °C |
1 hr |
| 18 % |
527 MPa |
465 MPa |
Ar (I1) EN |
730-760 °C |
1 hr |
| 23 % |
640 MPa |
550 MPa |
Ar (I1) EN |
730-760 °C |
1 hr |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
| 100 J |
20 °C |
Ar (I1) AWS |
- |
- |
| 80 J |
-20 °C |
Ar (I1) AWS |
- |
- |
| 50 J |
-29 °C |
Ar (I1) AWS |
- |
- |
| Stress relieved |
| Impact Value |
Testing Temperature |
保护气体 |
Stress Relieved Testing Temp |
Stress Relieved Testing Time |
| 230 J |
20 °C |
Ar (I1) AWS |
745 °C |
1 hr |
| 200 J |
-20 °C |
Ar (I1) AWS |
745 °C |
1 hr |
| 200 J |
-29 °C |
Ar (I1) AWS |
745 °C |
1 hr |
| 250 J |
20 °C |
Ar (I1) EN |
730-760 °C |
1 hr |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| 0.48 % |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
0.58 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
0.07 % |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.44 % |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.06 % |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
5.73 % |
熔敷数据
| 安培 |
直径 |
| 40-180 A |
1.6 mm |
| 60-200 A |
2.0 mm |
| 100-220 A |
2.4 mm |
| 130-250 A |
3.2 mm |