OK Tigrod 13.09是一种0.5Mo合金化镀铜焊丝，适用于诸如压力容器及锅炉内部管道等工作温度*高约500°C相同牌号抗蠕变钢的GTAW焊接。
Typical Tensile Properties
| PWHT 620°C 1h |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 28 % |
610 MPa |
510 MPa |
AWS Ar (I1) |
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 27 % |
620 MPa |
520 MPa |
AWS Ar (I1) |
| PWHT 620°C 1h |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 31 % |
550 MPa |
450 MPa |
EN Ar (I1) |
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 30 % |
600 MPa |
490 MPa |
EN Ar (I1) |
夏比V型缺口冲击性能
| PWHT 620°C 1h |
| Impact Value |
Testing Temperature |
保护气体 |
| 220 J |
-20 °C |
AWS Ar (I1) |
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
| 150 J |
-29 °C |
AWS Ar (I1) |
| 130 J |
-46 °C |
AWS Ar (I1) |
| PWHT 620°C 1h |
| Impact Value |
Testing Temperature |
保护气体 |
| 190 J |
20 °C |
EN Ar (I1) |
| 170 J |
-20 °C |
EN Ar (I1) |
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
| 180 J |
20 °C |
EN Ar (I1) |
| 160 J |
-20 °C |
EN Ar (I1) |
| 90 J |
-40 °C |
EN Ar (I1) |
| 25 J |
-60 °C |
EN Ar (I1) |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| 1.09 % |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
0.45 % |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
0.094 % |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
0.61 % |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
0.05 % |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ni |
Cr |
| - |
- |
- |
- |
- |
0.05 % |