OK 84.58是一款可熔敷半抗腐蚀马氏体钢的耐磨堆焊焊条。其无论冷却速度如何，均可在*焊道获得*高硬度。适合用于存在磨料磨损和冲击磨损零部件的耐磨堆焊，如农业机械、林业工具、装载机和搅拌机等。
焊缝金属分析
| Mn |
| Mn |
C |
Si |
Cr |
| 0.7 % |
- |
- |
- |
| C |
| Mn |
C |
Si |
Cr |
| - |
0.67 % |
- |
- |
| Si |
| Mn |
C |
Si |
Cr |
| - |
- |
0.7 % |
- |
| Cr |
| Mn |
C |
Si |
Cr |
| - |
- |
- |
10.4 % |
熔敷数据
| Fusion time per electrode at 90% I max |
kg weld metal/kg electrodes |
Number of electrodes/kg weld metal |
安培 |
熔敷率 |
电压 V |
直径 |
| 62 sec |
0.67 kg |
58 |
75-110 A |
1.0 kg/h |
23 V |
2.5 x 350 mm |
| 95 sec |
0.67 kg |
27 |
110-150 A |
1.4 kg/h |
23 V |
3.2 x 450 mm |
| 107 sec |
0.67 kg |
18 |
145-200 A |
1.9 kg/h |
24 V |
4.0 x 450 mm |
| 110 sec |
0.66 kg |
12 |
190-270 A |
2.8 kg/h |
26 V |
5.0 x 450 mm |