Austenitic manganese steel electrode with nickel for surfacing and building up mangnese steel components exposed to severe impact and moderate abrasion. The weld metal is less prone to embrittlement and cracking compared to plain austenitic manganese steel weld metal. Applications include: crusher plates and rolls, cones and mantels of rotary crushers, rail points.
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 30 % |
690 MPa |
440 MPa |
ISO |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
| 100 J |
20 °C |
ISO |
| 80 J |
-20 °C |
ISO |
| 45 J |
-80 °C |
ISO |
| 25 J |
-120 °C |
ISO |
焊缝金属分析
| Mn |
| Mn |
C |
Si |
Ni |
| 13.2 % |
- |
- |
- |
| C |
| Mn |
C |
Si |
Ni |
| - |
0.67 % |
- |
- |
| Si |
| Mn |
C |
Si |
Ni |
| - |
- |
0.2 % |
- |
| Ni |
| Mn |
C |
Si |
Ni |
| - |
- |
- |
3.0 % |
熔敷数据
| Fusion time per electrode at 90% I max |
kg weld metal/kg electrodes |
Number of electrodes/kg weld metal |
安培 |
熔敷率 |
电压 V |
直径 |
| 90 sec |
0.54 kg |
27 |
100-160 A |
1.5 kg/h |
30 V |
3.2 x 450 mm |
| 105 sec |
0.54 kg |
18 |
130-210 A |
2.0 kg/h |
30 V |
4.0 x 450 mm |
| 114 sec |
0.56 kg |
11 |
170-300 A |
2.9 kg/h |
31 V |
5.0 x 450 mm |