适用于焊接抗腐蚀无磁性及低温不锈钢的碱性药皮不锈钢焊条。该焊条可产生Mn和N含量较高的全奥氏体Cr-Ni-Mo焊缝金属。
Typical Tensile Properties
| As welded |
| Elongation |
Tensile Strength |
Yield Strength |
保护气体 |
| 35 % |
650 MPa |
450 MPa |
ISO |
夏比V型缺口冲击性能
| As welded |
| Impact Value |
Testing Temperature |
保护气体 |
| 90 J |
20 °C |
ISO |
| 50 J |
-196 °C |
ISO |
焊缝金属分析
| Mn |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| 6.5 % |
- |
- |
- |
- |
- |
- |
- |
| Mo |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
3.0 % |
- |
- |
- |
- |
- |
- |
| C |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
- |
0.04 % |
- |
- |
- |
- |
- |
| Si |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
- |
- |
0.5 % |
- |
- |
- |
- |
| Ferrite FN |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
- |
- |
- |
0 % |
- |
- |
- |
| Ni |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
- |
- |
- |
- |
16.0 % |
- |
- |
| Cr |
| Mn |
Mo |
C |
Si |
Ferrite FN |
Ni |
N |
Cr |
| - |
- |
- |
- |
- |
- |
- |
19.0 % |
熔敷数据
| Fusion time per electrode at 90% I max |
kg weld metal/kg electrodes |
Number of electrodes/kg weld metal |
安培 |
熔敷率 |
电压 V |
直径 |
| 72 sec |
0.62 kg |
46 |
70-100 A |
1.2 kg/h |
24 V |
3.2 x 350 mm |
| 74 sec |
0.64 kg |
29 |
100-140 A |
1.8 kg/h |
25 V |
4.0 x 350 mm |